Crystal

 Structure /Lattice Constant(A)

 M.P.
^oC

Density
g/cm³

Thermo-Expans
x10^-6/K

Dielectric constant

Lattice Mismatch to YBCO

Growth Tech & max. size

 LSAT

Cubic,  a=3.868

 1840

 6.74

 10

 22

0.82%

 CZ. 2"

 LaAlO₃

Rhombo. a=3.790 c=13.

 2100

 6.51

 9.2

 24.5

2.8%

 CZ 3"

 MgO

Cubic, a=4.21

 2852

 3.58

 12.8                

 9.80

7.9%

 Arc melt  2"

 NdCaAlO₄

Tetrag.a=3.685     c=12.12      

 1850

 5.56

 12.0

 19.5

5.5%

CZ 35mm

 NdGaO₃

Orthor.a=5.43b=5.50 c=7.71    

 1600

 7.57

 7.80

 25

1.1%

 CZ, 2"

 SrTiO₃

Cubic, a=3.905

 2080

 5.12

 10.4

 300

0.12%

 vernuil 30mm

 SrLaAlO₄

Tetrag.a=3.756 c=12.63

 1650

 5.92

 10.5

 16.8

3.7%

 CZ, 1"

 SrLaGaO₄

Orthor.a=5.176b=5.307c=7.355

 1600

 4.88

 2 ~ 10

 16~20

5.7%

 CZ, 1"

 YSZ

 Cubic, a=5.125

 ~2500

 5.80

 10.3

 27

31%

 Arc melt  2"