Dry 85120 Pouch Cell without Electrolyte (120mm x 85 mm), 5Ah - DPC85120

Dry 85120 pouch cell with various anode and cathode combinations can be used to evaluate the electrolyte diffusion effect, as well as prototype cell testing. 

Specification
    Battery Type                           Material Type           Testing Voltage Wondow (V)          Electroyte Filling Amount (Ah/g)           Inner Resistance as Reference (mΩ)

                                                      LFP + Graphite                            2.5 - 3.65                                              4.5                                                                 ≤ 18    
Dry 85120 Pouch Cell          
           5 Ah                                 NCM523 + Graphite                        3.0 - 4.3                                                3.5                                                                  ≤ 15
 
                                                    NFMO + Hard Carbon                      1.5 - 4.0                                                8.0                                                                  ≤ 15                                                    
                                                   (for sodium-ion battery)

  

Notes: 1. As for graphite electrode sheet, the active material portion is 93.2%, and area desnity for double side is 14.6 mg/cm2. The compaction desnity is1.4 g/cm3. 
           
           2. As for the LiFePO4 (LFP) electrode sheet, the active material portion is 95.4%, and area desnity for double side is 30.2 mg/cm2. The compaction desnity is 2.3 g/cm3.  

           3. As for the NCM523 electrode sheet, the active material portion is 95.5%, and area desnity for double side is 23 mg/cm2. The compaction desnity is 3.3 g/cm3.  
         
           4. As for the NFMO (NaNi1/3Fe1/3Mn1/3O2) electrode sheet, the active material portion is 95.5%, and area desnity for double side is 28.6 mg/cm2. The compaction desnity is 2.8 g/cm3
               As for the Hard Carbon (Kuraray Type2) electrode sheet, the active material portion is 92%, and area desnity for double side is 12.68 mg/cm2. The compaction desnity is 0.9 g/cm3

Testing Procedures:
           1. Electrolyte Filling with recommended amount in glovebox.
           2. First Time Aging : 45°C, formation time ≥ 15h in a oven.
           3. Formation conditions: 25°C, 5 min rest; 0.02C constant current charging; 0.1C constant current charging; Hot Press (eg: MSK-131-HS8)
           4. Second Time Aging: 45°C, formation time ≥ 24h in a oven
           5. Battery Analyzer for charging and discharging.

Application: These prototype pouch cell can be used to compare various electrode materials in the same cell structure, but also be useful for studying the electrolyte filling, distribution, and wetting.
                    Therefore the ultrasonic scanning imaging systems are good tools to study the above funamental projects.
                          UBSC-DTBT                                               UBSC-DT10                                   UBSC-LD50