Precursor Powder of NCMOH811 for High Capacity NCM Cathode Powder 200g/bottle - EQ-Lib-PNCM811
|
|
In stock
Item Number: Lib-PNCM811
|
Lib-PNCM811 is the precursor powder of NCMOH811 for High Capacity NCM Cathode Powder at your own composition.
There are 200 grams in one bottle
Note: You must mix the precursor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use
|
Specification
|
|
Package
|
200g/bottle in a vacuumed bag
|
|
Composition
|
NCMOH811
|
|
Configuration
|
Sphere
|
|
Particle size distribution
|
D10：5.36 μm
D50：11 μm
D90：18.6 μm
|
|
Magnetic substance
|
102 ppd
|
|
Tap Density
|
≥1.74 g/cm^3
|
|
Water Content
|
wt%＜0.5
|
|
|
|
|
PH value
|
~ 8.38
|
|
|
Mian Element
|
Required Content (mol)
|
Ratio (Ni:Co: Mn)
|
|
|
Li
|
0
|
0
|
|
|
Ni
|
47.7247
|
7.994
|
|
|
Co
|
6.3195
|
1.059
|
|
|
Mn
|
5.6562
|
0.947
|
|
|
Impurity
|
Required（ppm）
|
Typical（ppm）
|
|
|
Ca
|
＜300
|
16
|
|
|
Cu
|
＜50
|
1
|
|
|
Fe
|
＜100
|
15
|
|
|
Mg
|
＜300
|
2
|
|
|
Na
|
＜500
|
229
|
|
|
Zn
|
＜100
|
121
|
|
|
SO4
|
＜5000
|
3000
|
|
Note
|
MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have a question for IP, we will forward your inquiry to the producer.
|
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in a vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.
Related Products
|
|
|
|
Sale Price: Starting at USD$3,998.00
|
|
|
|
|
|
|
| |
|
| | |
|
Your cart is empty.
Please clear the browsing history before ordering the product. Otherwise, availability and price are not guaranteed. | |
| | |
|
MTI sponsorships:
MTI Sponsors Thermoelectrics Workshop
MTI-UCSD Battery Fabrication Lab
MTI-VISTEC Cylindrical Cell Pilot Line
MTI Sponsors the Postdoctoral Awards
Upcoming Shows:
|
|